Beige Crystallized Glass 2

Original Image

Product Name: Beige Crystallized Glass 2
Brand Name: TAKUCHI

Detailed Product Description: Beige Crystallized Glass 2

Crystallized glass
People also call it: pure white marble/Pure white artifical stone
Marmoglass / White crystal stone / crystal white glass / crystal glasses

1 Main materials: sand, silex, calcite, feldspar, sodium carbonate
2 Assistant materials: dolomite, barite, fluorite, etc.
3 Available slabs size: 2400-3200*1200-1400*11-29mm
4 Available tiles size: 300*300mm 600*600mm 610*610mm 910*910mm
11mm-18mm
5 Available colors: Beige, pure white
6 Water and slip resistance
7 Application: exterior/interior walls, floors,countertops, vanities, columns
Mitered ege in 45 degrees is necessary for countertop & vantiytop to avoid pore holes.
8 Feature:
1)Building material of green environment protection
2)no fading, contamination resistance
3)High hardness,acid/alkali resistance and wearability.
9 weight standard
11mm Standard panel: 30kg/m2
19 mm Standard panel: 53kg/m2
29mm Standard panel: 81kg/m2

Property Comparison with Other Relevant Materials
		Test Data	Documentary Data Granite
Property/Material	Unit	Crystallized Glass Panel	Marble	Granite
Specific gravity	g/cm3	2.65-2.7	2.5	2.7
Compression strength	Mpa	400	220	295
Rupture strength	Mpa	35	15	20
Charpy shock strength	Kj/M2	3.34	1.9	2.5
MohsHardness		6.0-6.5	3.50	5.5-6.0
Water absorption	%	0.02	0.3	0.35
coefficient Slip resistance	Dry	0.59
coefficient Slip resistance	Wet	0.36
Diffusion reflectivity	%	85	55	66
Acid-resistance	1%H2SO4,%	0.08	10.2	1
Alkali-resistance	1%NaOH,%	0.05	0.3	0.1
Thermal Expansion coefficient	X10-7/?	25-400?60	80-260	50-150
Radioactivity		No	Yes	Yes